                   Ex parte GEORGE D. CHANDLEY, RAYMOND F. RUFFINI                    
                                and NATHAN C. CROWELL                                 
                                                                                     
                                Appeal No. 2006-0594                                  
                             Application No. 09/740,708                               
                                                                                     
                                      ON BRIEF                                        
                                                                                     
          Before KIMLIN, PAK and KRATZ, Administrative Patent Judges.                 
          KIMLIN, Administrative Patent Judge.                                        

                                 DECISION ON APPEAL                                   
               This is an appeal from the final rejection of claims 10-24.            
          Claims 10 and 16 are illustrative:                                          
          10. A method of increasing the service life of a titanium                   
          aluminide alloy in contact with a molten metallic material                  
          comprising aluminum, comprising including in the titanium                   
          aluminide alloy a rare earth element in an effective amount to              
          prolong resistance to attack of the alloy by the molten metallic            
          material and contacting the alloy with the molten metallic                  
          material.                                                                   
          16. A method of prolonging resistance of a titanium aluminide               
          alloy to a molten metallic material comprising aluminum,                    
          comprising contacting the alloy for a time with the molten                  
          metallic material, removing the alloy from contact with the                 